RTM/Vacuum Leading Resin - Resin transfer molding(RTM) Leading Resin 9502P
● Resin transfer molding process:
RTM(Resin Transfer Molding) process is a form of composite liquid molding in which resin is mixed with a catalyst or hardener before being injected into a closed mold filled with reinforcing fibers.
● Performance and Application:
9502P low peak temperature,small shringage,high strength,fast post curing,water proof and heat resisting. Apply to small RTM or vacuum infusion product,such as FRP air conditioner,helmet,etc.
Code | Type | Viscosity Pa.s | Gel Time Mins | Tensile Strength Mpa | Tensile Modulus Mpa | Elongation at Break % | Flexural Strength Mpa | Flexural Modulus Mpa | Heat Deflection Temperature ℃ | Barcol Hardness |
9502P | orthophthalic tpye | 0.12-0.17 | 20-25 | 70 | 3500 | 2.5 | 120 | 3600 | 80 | 42 |
Executive Standard: GB/T8237-2005
● Notice:
1.The above index of resin is accordance with GB/T8237-2005 and JC/T1092-2008 stander, base on Neweco professional technical research and users experiences.Neweco reserve the right to modify its main parameters.
2.Unsaturated polyester resin is class 3 flammable, transfer and storage must comply with the relevant provisions of the State,prohibited exposure and rain.
3.UPR is unstable,store in a cool, ventilated warehouse.Keep away from fire and heat sources.The temperature should not exceed 30℃.The packaging requires a seal and must not come into contact with air.
● Product Cases: